we would use nylon vinyl, VERY low pressure 145c 3 seconds, peel off carrier, repress 15 seconds.
123 flex at 120c for 30 seconds would work but need more pressure and could peel off with time.
both products from TMT

logobear;112682 wrote:we would use nylon vinyl, VERY low pressure 145c 3 seconds, peel off carrier, repress 15 seconds.
123 flex at 120c for 30 seconds would work but need more pressure and could peel off with time.
both products from TMT

Cheers for that bear. Do you always use the nylon vinyl for bags like these? We have never used the nylon vinyl before so not sure about it. We have used 123/premium flex from TMT a lot and that has done a decent job on most items, including messenger style bags and the retro style ones which worked fine.

Have you ever tried transfers on similar items?

Cheers

nylon is magic and uber useful for anything with a PU coating.
It sticks lick F*** with no pressure